| PURE |
Type |
Ionic Form |
Moisture % |
Volume Capacity
mmol/ml |
Shipping Weight g/ml |
Particle Size % |
Comments |
| PA101 |
Poly-styrene Type I |
Cl- |
48-58 |
≥1.3 |
0.66-0.71 |
0.315-1.25mm ≥95 |
Standard Gel Type Ⅰ, SBA. High operating capacity. Good Kinetics and mechanical strength, good silica removal, used for condensate deionization and mixed bed, OH form also available. |
| PA102 |
Poly-styrene Type I |
Cl- |
42-48 |
≥1.5 |
0.67-0.73 |
0.315-1.25mm ≥95 |
| PA103 |
Poly-styrene Type II |
Cl- |
45-51 |
≥1.3 |
0.68-0.76 |
0.315-1.25mm ≥95 |
Standard Gel Type Ⅱ, SBA. Featuring very high capacity and regeneration efficiency.Greater resistance to organics than Type I resins.Excellent for 2 beds services;OH form also available. |
| PA104 |
Poly-styrene Type II |
Cl- |
37-44 |
≥1.5 |
0.68-0.76 |
0.315-1.25mm ≥95 |
| PA200 |
Poly-styrene Type I |
Cl- |
50-60 |
≥1.15 |
0.66-0.73 |
0.315-1.25mm ≥95 |
Macroporous Type Ⅰ, SBA. Good mechanical and osmotic resistance, well used for demineralization. Good silica removal.
OH form also available for immediate use. |
| PA201 |
Poly-styrene Type II |
Cl- |
47-57 |
≥1.2 |
0.68-0.73 |
0.315-1.25mm ≥95 |
Macroporous Type Ⅱ, SBA. High operating capacity. Especially for water source with higher salt content, decolorization of sugar liquor and separation of biochemicals. |
| PA501 |
Poly-acrylic |
Cl- |
55-65 |
≥1.2 |
0.68-0.75 |
0.315-1.25mm ≥95 |
Gel type, SBA,acrylic structure ensures excellent removal of organic matter. For demineralization of water and sugar decolorization. |
| PA502 |
Poly-acrylic |
Cl- |
55-65 |
≥1.2 |
0.68-0.75 |
0.315-1.25mm ≥95 |
Gel type, SBA,acrylic structure ensures excellent removal of organic matter. For demineralization of water and with the ability to remove both strong and weak acids from the solution. 。 |
| PA510 |
Poly-acrylic |
Cl- |
65-75 |
≥0.8 |
0.65-0.72 |
0.315-1.25mm ≥95 |
Macroporous type, acrylic SBA.Adsorbent resin for decolorization of organic solution. Organic scavenger. |